Double-Side Coated Alumina and LATP on PE Substrate Separator Roll as Flexible Solid-State Electrolyte (100 m L × 60 mm W × 15 um T) - Lib-LATP-AlPE6015

Double-Side Coated Alumina Ceramic and Li1.3 Al0.3 Ti1.7 (PO4)3 (LATP) on PE Substrate Separator Roll (100 m L × 60 mm W × 15 um T) that can be used as an excellent solid-state electrolyte separator for Li ion battery research. 

This flexible solid-state electrolyte roll can be used in our automatic stackers to prepare pouch cell and prismatic cell core.

    

Specifications

• Material: Double-Side Coated Al2O3 and Li1.3 Al0.3 Ti1.7 (PO4)3 (LATP) on   Polyethylene (PE) Substrate
  
• Thickness:                   15 ± 2 um (PE substrate: 9 um, 3 um Al2O3 and  3 um LATP)
• Width :                         60 ±0.5 mm
• Length:                        100 m (customized length can be supplied upon request)
• Air Permeability:        250±30 s/100cc
• Porosity:                     44 ± 5 %
• Area Density:             13.0±1.0 g/m2
• Puncture Strength :    ≥450 gf
• Tensile Strength:        ≥ 1800 Kgf/cm2 (MD);   ≥1700 Kgf/cm2 (TD)
• Thermal Shrinkage:    ≤2% (MD);   ≤1% (TD). Drying at 130℃ for 1 h. 
• Sold in roll only
•