MTI Corporation
LiNiCoAlO2 (Ni:Co:Al=8.15:1.5:0.35) Powder for High Power Li-ion Battery Cathode 200g/bottle - Lib-LNCA810
LiNiCoAlO2 (Ni:Co:Al=8.15:1.5:0.35) Powder for High Power Li-ion Battery Cathode 200g/bottle - Lib-LNCA810
LiNiCoAlO2 (Lithium Nickel Cobalt Aluminum Oxide) powder for Li-ion power battery cathode 200g/bottle (Ni:Co:Al =8.15:1.5:0.35)
Specification
| Item | Description | |
| Composition |
Li (NiCoAl) O2 Ni:Co:Al=8.15:1.5:0.35 |
Li = (7.2 ± 0.4)% Ni+Co+Al = (59.0 ± 1.0)% |
| D10 (μm) | 7.3 | |
| D50 (μm) | 13.6 | |
| D90 (μm) | 26.8 | |
| Dmax (μm) | 39.9 | |
| Moisture | 380 | |
| pH | 11.7 | |
| Li2CO3 (%) | 0.32 | |
| LiOH (%) | 0.11 | |
| Fe (ppm) | ≤100 ppm | |
| Na (ppm) | ≤200 ppm | |
| Cu (ppm) | ≤20 ppm | |
| Specific Surface Area (m2/g) | 0.5 | BET Analyzer |
| Tapped Density (g/cm3) | 2.40 | |
| Discharge Capacity (3.0-4.3V) (mAh/g) | 195.7 | @ 0.1C |
| Discharge Rate (%) | 90.0 | @2C vs.0.2C |
| Capacity Retention (RT, 3.0-4.3V, 1C/1C) (%) | 92.3 | 1C@51cls |
| Optional | You may order precursor to may your own composition ( click below link to order:
NiCoAl Precursor Powder (Ni0.8Co0.15Al0.05OH2 ) for DIY High Capacity Li-Ion Battery Cathode Powder 200g/bottle - EQ-Lib-Pre-NCA |
|
Application Notes:
- Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
- Please keep the powder in vacuum box to avoid moisture.
- Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity.
- This product is not manufactured by MTI. We only sell small quantity to help the researcher developing new battery. If you have any question on IP conflict, let us know. We will forward the question to the manufacturer.