LiNiCoMnO2 (Ni:Co:Mn=9: 0.5: 0.5) Powder for Li-ion Battery Cathode, 200g/bottle - Lib-LNCM911
LiNiCoMnO2 (Ni:Co:Mn=9: 0.5: 0.5) Powder for Li-ion Battery Cathode, 200g/bottle - Lib-LNCM911
Nickel-rich LiNiCoMnO2 (Lithium Nickel Cobalt Manganese Oxide, Ni:Co:Mn = 9:0.5:0.5) with advantages of higher energy density and lower cost, has attracted great attention in Li-ion battery compared to the LiCoO2 counterpart. Simultaneously, the Ni-rich NMC is good for the study of degradation mechanisms during charging/discharging processes.
Specification
Properties | Item | Standard Value |
Crystal Type | Polycrystalline | |
Chemical Composition |
Ni (mol%) | 90.0 ± 0.5 |
Co (mol%) | 5.0 ± 0.5 | |
Mn (mol%) | 5.0 ± 0.5 | |
Size Distribution |
D50 (μm) |
12.0 ± 1.0 |
Impurities (wt%) |
OH- |
≤0.30 |
CO32- | ≤0.20 | |
Specific Capacity (mAh/g) |
|
|
Coulombic Efficiency (%) |
|
|
Note |
|
- Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
- Please keep the powder in the vacuum box to avoid moisture.
- Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity.
- The product is for research only, not supply for large quantities,