Precursor Powder of NCMOH2 (Ni:Co:Mn = 9:0.5:0.5) for High Capacity NCM Cathode Powder, 200g/bottle - Lib-PNCM911
Precursor Powder of NCMOH2 (Ni:Co:Mn = 9:0.5:0.5) for High Capacity NCM Cathode Powder, 200g/bottle - Lib-PNCM911
Lib-PNCM911 is the precursor powder of NCMOH with Ni:Co:Mn = 9 : 0.5: 0.5 for High Capacity NCM Cathode Powder.
There are 200 grams in one bottle
Note: You must mix the precursor with LiOH. H2O and calcine the mixed powder at 750- 790 °C before use
Specification
|
Package |
|
||
|
Composition |
|
||
|
Configuration |
|
||
|
Particle Size Distribution |
|
||
|
Tap Density |
|
||
|
Main Element |
Standard Content (mol%) |
Measured Content (mol%) |
|
|
Chemical Composition |
Ni |
90.00 ± 1 |
90.11 |
|
Co |
5 ± 1 |
5.92 |
|
|
Mn |
5 ± 1 |
3.98 |
|
|
Impurity |
Standard Content (ppm) |
Measured Content (ppm) |
|
|
Fe |
3 |
2 |
|
|
Ca |
8 |
7 |
|
|
Mg |
8 |
7 |
|
|
Cu |
2 |
0 |
|
|
Na |
500 |
351 |
|
|
H2O |
- |
3700 |
|
|
Note |
MTI does not manufacture this product, and only sell a small quantity to research the development of new-generation battery. If you need a larger amount or have a question about IP, we will forward your inquiry to the producer.
|
||
Application Notes:
- Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
- Please keep the powder in a vacuum box to avoid moisture.
- Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity.