Single-Side Coated LATP on PE Substrate Separator Roll as Flexible Solid-State Electrolyte (100 m L × 60 mm W × 16 um T) - Lib-LATP-PE6016

Single-Side Coated LATP on PE Substrate Separator Roll as Flexible Solid-State Electrolyte (100 m L × 60 mm W × 16 um T) - Lib-LATP-PE6016

Single-Side Coated Li1.3 Al0.3 Ti1.7 (PO4)3 (LATP) on PE Substrate Separator Roll (100 m L × 60 mm W × 16 um T) that can be used as an excellent solid-state electrolyte separator for Li ion battery research. 

This flexible solid-state electrolyte roll can be used in our automatic stackers to prepare pouch cell and prismatic cell core.

Bench-Top Automatic Pouch Cell Stacking Machine up to 110 mm L x 100 mm W - MSK-111A-ES    

Specifications

  • Material: Single-Side Coated Li1.3Al0.3Ti1.7(PO4)3 (LATP) on Polyethylene (PE)
  • Thickness:                   16 ± 2 um (PE substrate: 12 um and 4 um LATP)
  • Width :                         60 ±0.5 mm
  • Length:                       100 m (customized length can be supplied upon request)
  • Air Permeability:        228 s/100mL
  • Porosity:                     42 %
  • Area Density:             13.0±1.0 g/m2
  • Puncture Strength :    ~391 gf
  • Tensile Strength:        ~1310 Kgf/cm2 (MD);   ~1223 Kgf/cm2 (TD)
  • Thermal Shrinkage:    ~1.5% (MD);   ~0.7% (TD). Drying at 130℃ for 1 h. 
  • Sold in roll only