Li-Ion Battery Cathode - Aluminum Foil Single Side Coated by LiFePO4 (LFP, 241mm L x 200mm W x 84um Thickness) 5 sheets/bag - bcaf-lpfss

Li-Ion Battery Cathode - Aluminum Foil Single Side Coated by LiFePO4 (LFP, 241mm L x 200mm W x 84um Thickness) 5 sheets/bag - bcaf-lpfss

This electrode sheet is based on Aluminum foil coated by lithium iron phosphate (LiFePO4, LFP) in single side and is used as the cathode of Li-Ion battery - 5 sheets /bag
Note: This electrode sheets and its parameters were updated from Oct. 2023.


SPECIFICATIONS

  • Current collector (substrate): Aluminum foil (16 microns)
  • Cathode material: lithium ferrous phosphate (coated by carbon)
  • Length: 241mm, Width: 175mm ( The edge width of blank area is 12.5 mm for each side)
  • Single Side Coating Area Density: 13.5±0.2 mg/cm2
  • Compaction Density of Coating: 2.0±0.1g/cm3
  • Current Collector Area Density: 4.22 mg/cm2
  • Coating thickness: ~68 um
  • Total Thickness: ~84 um (after hot calendaring)
  • Active Material Weight: 5.43 g
  • Active Material Ratio in powder: 95.4% (PVDF and Super P is 2% and 2.6%, respectively)
  • Specific Capacity: 150 mAh/g (Area Capacity: 1.932 mAh/cm2); 0.1 C; 2.5-3.7 V;  Electrolyte: 1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC
  • Charging and Discharging Curve for the First Cycle
  • Rate Testing
  • Cycling Test
  • Note: Please vacuum heated dry (100oC) before assembling the battery
 for aluminum     
 for LiFePO4


Please click the video below to see how        