Li-S Battery Cathode - Aluminum Foil Double Side Coated by Sulfur-Carbon (S/C) Composite (80mm L x 50mm W), 5 sheets/bag - bcaf-SCC-ds

Li-S Battery Cathode - Aluminum Foil Double Side Coated by Sulfur-Carbon (S/C) Composite (80mm L x 50mm W), 5 sheets/bag - bcaf-SCC-ds

This electrode sheet is based on Aluminum foil coated by S/C composite. Sulfur-Carbon Composite (S/C) with high conductity and uniform mixing features can be used as high performance cathode for Li-S battery testing

SPECIFICATIONS

  • Material: S/C Composite 
  • Current collector (substrate): Aluminum foil (16 microns, area desnity of 4.22mg/cm2)
  • Coated Area: 80mm L x 50mm W.
  • Double sides area density: 8,2 ± 0.2 mg/cm2
  • Compaction density: 3.4 ± 0.1 g/cm3
  • Coating Thickness: ~66 um
  • Total Thickness: ~82 um
  • Active Material Weight: 8.23 g
  • Active Material Proportion in Powder: 94% 
  • Specific Capacity: ~1260 mAh/g (0.25C), ~1100 mAh/g (0.5C). [DOL:DME =1:1, 1 mol/L LiTFSI, testing voltage range: 1.5-2.6 V]
     
  • Note:  The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.