LiNiCoMnO2 (Ni:Co:Mn=6:2:2, NCM622) Powder for High Power Li-ion Battery Cathode, 200g/bottle-EQ-Lib-LNCM622

LiNiCoMnO2 (Ni:Co:Mn=6:2:2, NCM622) Powder for High Power Li-ion Battery Cathode, 200g/bottle-EQ-Lib-LNCM622

LiNiCoMnO2 (Lithium Nickel Manganese Cobalt Oxide) powder for Li-ion battery cathode, 200g/bottle (Ni : Co : Mn = 6 : 2 : 2, NCM622 or NMC622). 

Specification

Properties Item Measured Value Standard Value

Chemical Composition
Li (Wt%) 7.2±0.6 7.4
Ni+Co+Mn (Wt%) 59.0±1.0 58.6

Impurities
Na (ppm)

≤100

20
Fe (ppm)

≤100

30
Cu (ppm)

≤50

1

Size Distribution

D10 (μm)

≥5.0

6.6
D50 (μm)

11±2

11.0
D90 (μm)

≤28

18

Dmax(μm)

≤45 28.9
Specific Surface Area (m2/g) 0.35±0.15 0.27
Tap Density (g/cm³) ≥2.1 2.65
Moisture (ppm) ≤400 300
pH 11.0~12.0 11.56

Electrochemical Properties
First discharge specific capacity (2032 coin battery, 0.1C/0.1C, 2.8-4.25V, mAh/g) ≥5.0 176.0
First charge and discharge efficiency (%) ≥85.0 89
Charge & Discharge Plot
CDC
SDS


Note: MTI does not manufacture this product, and only sells a small quantity to research for the development of new generation batteries. If you need a larger quantity or have a question about the IP, we will forward your inquiry to the producer.

Application Notes:

  1. Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
  2. Please keep the powder in a vacuum box to avoid moisture.
  3. Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity.